Bulletin, 5. ciltAmerican Society for Testing and Materials., 1905 Vols. 1-61 include reports of the 1st-64th annual meetings, committee reports and technical papers; v.16-38 include also "New and revised tentative standards [and] tentative revisions of standards" (varies slightly) |
Kitabın içinden
67 sonuçtan 1-5 arası sonuçlar
Sayfa 26
... length of fine wire followed it . On taking out a transverse slice of the axle at this point , a cavity was found in the metal , which would hold half a pint or more . The walls of the cavity were perfectly clean and bright , and but ...
... length of fine wire followed it . On taking out a transverse slice of the axle at this point , a cavity was found in the metal , which would hold half a pint or more . The walls of the cavity were perfectly clean and bright , and but ...
Sayfa 30
... length of time in advance of the next annual meeting to give ample opportunity for written discussion . " In pursuance of this action a meeting of Committee A was held in Philadelphia on December 9-10 , 1904. This meeting was attended ...
... length of time in advance of the next annual meeting to give ample opportunity for written discussion . " In pursuance of this action a meeting of Committee A was held in Philadelphia on December 9-10 , 1904. This meeting was attended ...
Sayfa 33
... length owing to the lack of suitable transportation equipment on the part of the railroads , especially in the East , for handling rails 33 feet long . Moreover , the 30 foot length is better adapted to the usual size of ingot for 100 ...
... length owing to the lack of suitable transportation equipment on the part of the railroads , especially in the East , for handling rails 33 feet long . Moreover , the 30 foot length is better adapted to the usual size of ingot for 100 ...
Sayfa 39
... length of at least 9 inches , with enlarged ends . 6. Rivet rods shall be tested as rolled . Rivets . 7. Specimens shall be cut from the finished rolled or forged Pins and Rollers . bar in such manner that the center of the specimen ...
... length of at least 9 inches , with enlarged ends . 6. Rivet rods shall be tested as rolled . Rivets . 7. Specimens shall be cut from the finished rolled or forged Pins and Rollers . bar in such manner that the center of the specimen ...
Sayfa 40
... lengths of the full section of the bar . 10. At least one tensile and one bending test shall be made from each melt of steel as rolled . In case steel differing inch and more in thickness is rolled from one melt , a test shall be made ...
... lengths of the full section of the bar . 10. At least one tensile and one bending test shall be made from each melt of steel as rolled . In case steel differing inch and more in thickness is rolled from one melt , a test shall be made ...
İçindekiler
7 | |
17 | |
30 | |
46 | |
63 | |
75 | |
101 | |
130 | |
308 | |
316 | |
319 | |
331 | |
335 | |
363 | |
381 | |
388 | |
165 | |
171 | |
179 | |
191 | |
198 | |
213 | |
221 | |
234 | |
254 | |
257 | |
268 | |
275 | |
283 | |
294 | |
304 | |
417 | |
426 | |
436 | |
445 | |
453 | |
458 | |
470 | |
496 | |
512 | |
520 | |
540 | |
555 | |
556 | |
561 | |
Diğer baskılar - Tümünü görüntüle
Sık kullanılan terimler ve kelime öbekleri
28 days absorption American Society Annual Meeting Asphalt Association for Testing average Bauzeitung beam bricks briquettes Building carbon Carnegie Steel Company cars Cast Iron cent Chairman chemical Chemist Chicago Civil Engineer coat compression Congress Consulting Engineer cracks cubes deflection elastic limit ELECTED elongation Executive Committee extensometer Foundry grades Gray Iron heat inch increase inspection Inspector International Association investigation Iron and Steel laboratory Lesley linseed oil load manufacturer Mass membership metal mixture modulus of elasticity mortar natural cement neat obtained paint Pennsylvania Railroad Philadelphia pig iron pigment Pittsburg Portland cement pounds President Professor Proposed Standard Specifications Railroad rails Railway reinforced concrete samples sand Schweiz Secretary Society for Testing Specifications for Steel specimen staybolt Steel Company Street stresses structural sulphur Superintendent surface temperature tensile strength tension test piece testing machine Testing Materials Thermit tion torsion wheel York Zürich
Popüler pasajlar
Sayfa 450 - AMERICAN SOCIETY FOR TESTING MATERIALS EXTRACT FROM CHARTER 1. The name of the proposed corporation is the "American Society for Testing Materials." 2. The corporation is formed for the promotion of knowledge of the materials of engineering, and the standardization of specifications and the methods of testing.
Sayfa 110 - Engineers, the American Society of Civil Engineers and the American Society for Testing Materials.
Sayfa 45 - The inspector representing the purchaser shall have all reasonable facilities afforded to him by the manufacturer to satisfy him that the finished material is furnished in accordance with these specifications.
Sayfa 213 - Ibs. 7 days (1 day in moist air, 6 days in water) 500 Ibs. 28 days (1 day in moist air, 27 days in water) 600 Ibs. One Part Cement, Three Parts Standard Ottawa Sand.
Sayfa 365 - The test piece shall be adjusted, so that the center of its upper surface is tangent to the spherical end of the plunger.
Sayfa 62 - No. 8 sieve, with a mixture of one to twelve bituminous facing. The mold shall be rammed evenly and fairly hard, thoroughly dried and not cast until it is cold. The test bar shall not be removed from the mold until cold enough to be handled.
Sayfa 355 - Conference was established by the Institution of Civil Engineers, the Institution of Mechanical Engineers, the Institution of Electrical Engineers, the Institute of...
Sayfa 62 - Л inch smaller in diameter than the top, to allow for draft and for the strain of pouring. The pattern shall not be rapped before withdrawing. The flask is to be rammed up with green molding sand, a little damper than usual, well mixed and put through a No.
Sayfa 38 - Chemical determinations of the percentages of carbon, phosphorus, sulphur and manganese shall be made by the manufacturer from a test ingot taken at the time of the pouring of each melt of steel, and a correct copy of such analysis shall be furnished to the engineer or his inspector.
Sayfa 42 - ... is manufactured. He shall furnish a suitable testing machine for testing the specimens, as well as prepare the pieces for the machine, free of cost.