Bulletin, 5. ciltAmerican Society for Testing and Materials., 1905 Vols. 1-61 include reports of the 1st-64th annual meetings, committee reports and technical papers; v.16-38 include also "New and revised tentative standards [and] tentative revisions of standards" (varies slightly) |
Kitabın içinden
100 sonuçtan 1-5 arası sonuçlar
Sayfa 62
... loading , and will be taken at that point where the proportionality changes . 10. Turnings from the tensile specimen or drillings from the bending specimen or drillings from the small test ingot , if preferred by the inspector , shall ...
... loading , and will be taken at that point where the proportionality changes . 10. Turnings from the tensile specimen or drillings from the bending specimen or drillings from the small test ingot , if preferred by the inspector , shall ...
Sayfa 67
... load and ship the wheels promptly . Wheels offered for inspection must not be covered with any substance which will hide defects . 9. A hundred or more wheels being ready for test , the Inspec- Retaping . Drop Tests . tor will make a ...
... load and ship the wheels promptly . Wheels offered for inspection must not be covered with any substance which will hide defects . 9. A hundred or more wheels being ready for test , the Inspec- Retaping . Drop Tests . tor will make a ...
Sayfa 71
... load shall be not under : Properties . Light castings .. Medium castings Heavy castings 2,500 lbs . 2,900 3,300 " 4 In no case shall the deflection be under .10 of an inch . Tensile Test . Where specified , this shall not run less than ...
... load shall be not under : Properties . Light castings .. Medium castings Heavy castings 2,500 lbs . 2,900 3,300 " 4 In no case shall the deflection be under .10 of an inch . Tensile Test . Where specified , this shall not run less than ...
Sayfa 72
... load applied at the middle , and the deflection at rupture noted . One bar of every two of each set made must fulfill the requirements to permit acceptance of the castings represented . 8. The mold for the bars is shown in Fig . 2. The ...
... load applied at the middle , and the deflection at rupture noted . One bar of every two of each set made must fulfill the requirements to permit acceptance of the castings represented . 8. The mold for the bars is shown in Fig . 2. The ...
Sayfa 73
... load shall be from 20 to 40 Speed of Testing . seconds for a deflection of 0.10 inch . - ¥ " ; 15 " Pattern . Pouring Basin 10 " Pipe bored with vent holes 10 " Pipe cope 10. Borings from the broken pieces of the " Arbitration Bar ...
... load shall be from 20 to 40 Speed of Testing . seconds for a deflection of 0.10 inch . - ¥ " ; 15 " Pattern . Pouring Basin 10 " Pipe bored with vent holes 10 " Pipe cope 10. Borings from the broken pieces of the " Arbitration Bar ...
İçindekiler
7 | |
17 | |
30 | |
46 | |
63 | |
75 | |
101 | |
130 | |
308 | |
316 | |
319 | |
331 | |
335 | |
363 | |
381 | |
388 | |
165 | |
171 | |
179 | |
191 | |
198 | |
213 | |
221 | |
234 | |
254 | |
257 | |
268 | |
275 | |
283 | |
294 | |
304 | |
417 | |
426 | |
436 | |
445 | |
453 | |
458 | |
470 | |
496 | |
512 | |
520 | |
540 | |
555 | |
556 | |
561 | |
Diğer baskılar - Tümünü görüntüle
Sık kullanılan terimler ve kelime öbekleri
28 days absorption American Society Annual Meeting Asphalt Association for Testing average Bauzeitung beam bricks briquettes Building carbon Carnegie Steel Company cars Cast Iron cent Chairman chemical Chemist Chicago Civil Engineer coat compression Congress Consulting Engineer cracks cubes deflection elastic limit ELECTED elongation Executive Committee extensometer Foundry grades Gray Iron heat inch increase inspection Inspector International Association investigation Iron and Steel laboratory Lesley linseed oil load manufacturer Mass membership metal mixture modulus of elasticity mortar natural cement neat obtained paint Pennsylvania Railroad Philadelphia pig iron pigment Pittsburg Portland cement pounds President Professor Proposed Standard Specifications Railroad rails Railway reinforced concrete samples sand Schweiz Secretary Society for Testing Specifications for Steel specimen staybolt Steel Company Street stresses structural sulphur Superintendent surface temperature tensile strength tension test piece testing machine Testing Materials Thermit tion torsion wheel York Zürich
Popüler pasajlar
Sayfa 450 - AMERICAN SOCIETY FOR TESTING MATERIALS EXTRACT FROM CHARTER 1. The name of the proposed corporation is the "American Society for Testing Materials." 2. The corporation is formed for the promotion of knowledge of the materials of engineering, and the standardization of specifications and the methods of testing.
Sayfa 110 - Engineers, the American Society of Civil Engineers and the American Society for Testing Materials.
Sayfa 45 - The inspector representing the purchaser shall have all reasonable facilities afforded to him by the manufacturer to satisfy him that the finished material is furnished in accordance with these specifications.
Sayfa 213 - Ibs. 7 days (1 day in moist air, 6 days in water) 500 Ibs. 28 days (1 day in moist air, 27 days in water) 600 Ibs. One Part Cement, Three Parts Standard Ottawa Sand.
Sayfa 365 - The test piece shall be adjusted, so that the center of its upper surface is tangent to the spherical end of the plunger.
Sayfa 62 - No. 8 sieve, with a mixture of one to twelve bituminous facing. The mold shall be rammed evenly and fairly hard, thoroughly dried and not cast until it is cold. The test bar shall not be removed from the mold until cold enough to be handled.
Sayfa 355 - Conference was established by the Institution of Civil Engineers, the Institution of Mechanical Engineers, the Institution of Electrical Engineers, the Institute of...
Sayfa 62 - Л inch smaller in diameter than the top, to allow for draft and for the strain of pouring. The pattern shall not be rapped before withdrawing. The flask is to be rammed up with green molding sand, a little damper than usual, well mixed and put through a No.
Sayfa 38 - Chemical determinations of the percentages of carbon, phosphorus, sulphur and manganese shall be made by the manufacturer from a test ingot taken at the time of the pouring of each melt of steel, and a correct copy of such analysis shall be furnished to the engineer or his inspector.
Sayfa 42 - ... is manufactured. He shall furnish a suitable testing machine for testing the specimens, as well as prepare the pieces for the machine, free of cost.