Л inch smaller in diameter than the top, to allow for draft and for the strain of pouring. The pattern shall not be rapped before withdrawing. The flask is to be rammed up with green molding sand, a little damper than usual, well mixed and put through... Bulletin - Sayfa 62American Society for Testing Materials tarafından - 1905Tam görünüm - Bu kitap hakkında
| Gaetano Lanza - 1905 - 980 sayfa
...represented. The mold for the bars is shown in Fig. 2 (not shown here). The bottom of the bar is TJ of an inch smaller in diameter than the top, to allow...withdrawing. The flask is to be rammed up with green molding-sand, a little damper than usual, well mixed and put through a No. 8 sieve, with a mixture... | |
| American Society for Testing Materials - 1910 - 326 sayfa
...represented. Mold for Test Bar. 8. The mold for the bars is shown in Fig. 2. The bottom of the bar is A inch smaller in diameter than the top, to allow for...molding sand, a little damper than usual, well mixed and Pattern. -tf-t ±13 Speed of Tasting. FIG. 2. — MOLD FOR ARBITRATION TEST BAR. put through a No.... | |
| 1911 - 262 sayfa
...requirements to permit the acceptance of the castings represented. The bottom of the bar is one-sixteenth of an inch smaller in diameter than the top, to allow...withdrawing. The flask is to be rammed up with green molding-sand, a little damper than usual, well mixed and put through a number eight sieve, with a mixture... | |
| 1913 - 420 sayfa
...represented. 8. The mold for the bars is shown in Fig. 2. The bottom of Moid for Test the bar is jV inch smaller in diameter than the top, to allow for...molding sand, a little damper than usual, well mixed and Pattern. Bart— Utf 1 m FIG. 2. — MOLD FOR ARBITRATION TTST BAR. put through a No. 8 sieve, with... | |
| American School of Correspondence, Chicago, F. W. Fitzpatrick - 1913 - 148 sayfa
...fulfill the requirements to permit acceptance of the castings represented. fThe bottom of the bar is y'j of an inch smaller in diameter than the top, to allow...withdrawing. The flask is to be rammed up with green moulding-sand, a little damper than usual, well mixed and put through a No. 8 sieve with a mixture... | |
| Henry Jackson Burt - 1914 - 408 sayfa
...represented. The mold for the bars is shown in Fig. 2 (figure not given.). The bottom of the bar is Л inch smaller in diameter than the top, to allow for...molding sand, a little damper than usual, well mixed and put through a No. 8 sieve, with a mixture of one to twelve bituminous facing The mold shall be rammed... | |
| Milo Smith Ketchum - 1914 - 958 sayfa
...8. Mold for Test Bar. The mold for the bars is shown in Fig. 2. The bottom of the bar is •fa in. smaller in diameter than the top, to allow for draft...molding sand, a little damper than usual, well mixed and put through a No. 8 sieve, with a mixture of one to twelve bituminous facing. The mold shall be rammed... | |
| American Railway Master Mechanics' Association - 1915 - 880 sayfa
...(a) ARBITRATION BAR.— The mold for the bars is shown in Figure I . The bottom of the bar is sfg in. smaller in diameter than the top, to allow for draft...molding sand, a little damper than usual, well mixed and put through a No. 8 sieve, with a mixture of I to 12 bituminous facing. The mold shall be rammed evenly... | |
| American Society of Mechanical Engineers - 1915 - 1412 sayfa
...106 Mold for Test Bar. The mold for the bars is shown in Fig. 6. The bottom of the bar is 1/16 in. smaller in diameter than the top, to allow for draft...molding sand, a little damper than usual, well mixed and put through a No. 8 sieve, with a mixture of one to twelve bituminous facing. The mold shall be rammed... | |
| |