No. 8 sieve, with a mixture of one to twelve bituminous facing. The mold shall be rammed evenly and fairly hard, thoroughly dried and not cast until it is cold. The test bar shall not be removed from the mold until cold enough to be handled. Bulletin - Sayfa 62American Society for Testing Materials tarafından - 1905Tam görünüm - Bu kitap hakkında
| Gaetano Lanza - 1905 - 980 sayfa
...The flask is to be rammed up with green molding-sand, a little damper than usual, well mixed and put through a No. 8 sieve, with a mixture of one to twelve...thoroughly dried and not cast until it is cold. The test-bar shall not be removed from the mold until cold enough to be handled. SPEED OF TESTING. The... | |
| American Railway Master Mechanics' Association - 1906 - 662 sayfa
...sand, a little damper than usual, well mixed and put through a No. 8 sieve with a mixture of i to 12 bituminous facing. The mold shall be rammed evenly...removed from the mold until cold enough to be handled. The rate of application of the load shall be from 20 to 40 seconds for a deflection of o.1o inch. Borings... | |
| 1909 - 714 sayfa
...sand, a little damper than usual, well mixed and put through a No. 8 sieve with a mixture of 1 to 12 bituminous facing. The mold shall be rammed evenly...removed from the mold until cold enough to be handled. The rate of application of the load shall be from 20 to 40 seconds for a deflection of 0.10 in. Borings... | |
| American Railway Master Mechanics' Association - 1909 - 484 sayfa
...sand, a little damper than usual, well mixed and put through a No. 8 sieve with a mixture of I to 12 bituminous facing. The mold shall be rammed evenly...it is cold. The test bar shall not be removed from flie mold until cold enough to be handled. The rate of application of the load shall be from 20 to... | |
| American Society for Testing Materials - 1910 - 326 sayfa
...well mixed and Pattern. -tf-t ±13 Speed of Tasting. FIG. 2. — MOLD FOR ARBITRATION TEST BAR. put through a No. 8 sieve, with a mixture of one to twelve...removed from the mold until cold enough to be handled. 10. Borings from the broken pieces of the "Arbitration Bar" samples for shall be used for the sulphur... | |
| 1911 - 262 sayfa
...rammed up with green molding-sand, a little damper than usual, well mixed and put through a number eight sieve, with a mixture of one to twelve bituminous...thoroughly dried and not cast until it is cold. The test-bar shall not be removed from the mold until cold enough to be handled. Sect, 1 1 7. Tests of... | |
| 1913 - 420 sayfa
...than usual, well mixed and Pattern. Bart— Utf 1 m FIG. 2. — MOLD FOR ARBITRATION TTST BAR. put through a No. 8 sieve, with a mixture of one to twelve...shall be rammed evenly and fairly hard, thoroughly drie 1 an.l not cast until it is cold. The test bar shall not Ix- removed from the mold until cold... | |
| American School of Correspondence, Chicago, F. W. Fitzpatrick - 1913 - 148 sayfa
...The flask is to be rammed up with green moulding-sand, a little damper than usual, well mixed and put through a No. 8 sieve with a mixture of one to twelve bituminous facing. The mould shall be rammed evenly and fairly hard, thoroughly dried and not cast until it is cold. The test-bar... | |
| Henry Jackson Burt - 1914 - 410 sayfa
...The flask is to be rammed up with green molding sand, a little damper than usual, well mixed and put through a No. 8 sieve, with a mixture of one to twelve...removed from the mold until cold enough to be handled. The rate of application of the load shall be from 20 to 40 seconds for a deflection of 0.10 inch. Borings... | |
| |