Hydraulic Cement: Its Properties, Testing, and UseJ. Wiley & sons, 1906 - 300 sayfa |
Diğer baskılar - Tümünü görüntüle
Sık kullanılan terimler ve kelime öbekleri
28 days action aluminate of lime American Society apparatus briquettes burning calcium sulphate Candlot carbonate carbonic acid celit cement mortar cent centimeters Chatelier Chemical Civil Engineers clinker commonly concrete consistency contain cracks days in water determined diameter disintegration effect Elements employed expansion Fahr free lime gauging give grains grammes grappiers hardening heat hydrated hydraulic index hydraulic lime immersed inert iron kiln laboratory Le Chatelier less machine magnesia Manual Mechanics millimeters mixed mixture morocco mould natural cements neat cement needle obtained oxide pats placed Portland cement powder practice Prof proportion quantity of water quick-setting quicklime rate of setting recommended Roman cements sand mortar sea-water sieve silica silica and alumina slag cement slaked lime slaking slow-setting Society of Civil specific gravity specimen standard sand Strength of Materials sulphate sulphuric acid swelling temperature tensile strength Testing Materials tion Treatise tricalcic unsoundness usually varies volume weight
Popüler pasajlar
Sayfa 307 - Surveying Instruments i2mo, 3 oo Bixby's Graphical Computing Table Paper 19^X24! inches. 25 ** Burr's Ancient and Modern Engineering and the Isthmian Canal. (Postage, 27 cents additional.) 8vo...
Sayfa 309 - Fuertes's Water and Public Health 12mo, 1 50 Water-filtration Works 12mo. 2 50 Ganguillet and Kutter's General Formula for the Uniform Flow of Water in Rivers and Other Channels.
Sayfa 162 - Care should be observed in centering the briquettes in the testing machine, as cross-strains, produced by improper centering, tend to lower the breaking strength. The load should not be applied too suddenly, as it may produce vibration, the shock from which often breaks the briquette before the ultimate strength is reached.
Sayfa 265 - F. as practicable, and observed at intervals for at least 28 days. (c) A third pat is exposed in any convenient way in an atmosphere of steam, above boiling water, in a loosely closed vessel for five hours. (24) These pats, to satisfactorily pass the requirements, shall remain firm and hard and show no signs of distortion, checking, cracking or disintegrating.
Sayfa 265 - Pats of neat cement about three inches in diameter, one-half inch thick at the center, and tapering to a thin edge, shall be kept in moist air for a period of twenty-four hours.
Sayfa 304 - Chase's Screw Propellers and Marine Propulsion „ 8vo, 3 oo Cloke's Gunner's Examiner .' 8vo, i 50 Craig's Azimuth 4to, 3 50 Crehore and Squier's Polarizing Photo-chronograph 8vo, 3 oo * Davis's Elements of Law 8vo, 2 50 * Treatise on the Military Law of United States 8vo, 7 oo Sheep, 7 50 De Brack's Cavalry Outposts Duties.
Sayfa 310 - Engineering" and Electric Traction Pocket-book. . i6mo, morocco, 5 oo Dredge's History of the Pennsylvania Railroad: (1879) Paper, 5 oo * Drinker's Tunnelling, Explosive Compounds, and Rock Drills. 4to, half mor., 25 oo Fisher's Table of Cubic Yards Cardboard, 25 Godwin's Railroad Engineers' Field-book and Explorers
Sayfa 264 - It shall develop initial set in not less than thirty minutes, but must develop hard set in not less than one hour, nor more than ten hours. TENSILE STRENGTH 22. The minimum requirements for tensile strength for briquettes one inch square in section shall be within the following limits, and shall show no retrogression in strength within the periods specified: ' Age Neat Cement Strength 24 hours in moist air 150 — 200 Ibs.